NO10-1270N Data sheet数据表
极薄无取向电工钢
Cogent Hi-Lite NO10-1270N牌号符合EN 10303:2015和IEC 60404-8-8:2017标准中的所有要求。 在许多情况下,最小/最大性能优于上述标准中相同牌号标称厚度的等级。
Magnetic properties 磁性
| 最小值/最大值 | 典型值
|
Specific total loss特定总铁损值 at 1.0 T and 50 Hz | - | 1.10 W/kg |
Specific total loss特定总铁损值 at 1.5 T and 50 Hz | - | 2.84 W/kg |
Specific total loss特定总铁损值 at 1.0 T and 400 Hz | Max 12.7 W/kg | 11.0 W/kg |
Specific total loss特定总铁损值 at 1.5 T and 400 Hz | Max 30.9 W/kg | 28.5 W/kg |
Specific total loss特定总铁损值 at 1.0 T and 700 Hz | Max 23.6 W/kg | 21.6 W/kg |
Specific total loss特定总铁损值 at 1.0 T and 2500 Hz | - | 123 W/kg |
Peak magnetic polarisation磁极化峰值 at 2500 A/m and 50 Hz | Min 1.52 T | 1.56 T |
Peak magnetic polarisation磁极化峰值 at 5000 A/m and 50 Hz | Min 1.63 T | 1.66 T |
Peak magnetic polarisation磁极化峰值 at 10000 A/m and 50 Hz | Min 1.76 T | 1.79 T |
Relative peak permeability相对峰值渗透率 at 1.5 T and 50 Hz | - | 770 |
Relative peak permeability相对峰值渗透率 at 1.0 T and 400 Hz | - | 6200 |
保证铁损值是最大特定总损耗,磁极化的保证值是最小磁极化峰值
物理和机械性能
厚度0.10 mm 密度(假设)7.65 kg / dm3
| 最小值/最大值 | 典型值
|
Electrical resistivity at 23 °C 在23 °C的电阻率 | - | 51 µΩ·cm |
Thermal conductivity at 23 °C 在23 °C的导热系数 | - | 23 W/(m·K) |
Thermal expansion热膨胀 0-100 °C | - | 12·10-6 /°C |
|
|
|
Yield strength 屈服强度Rp0.2 | Min 330 MPa | 370 MPa |
Tensile strength抗拉强度 Rm | Min 430 MPa | 470 MPa |
Elongation at fracture 断裂伸长率A80 | Min 14 % | 19 % |
Young’s modulus杨氏模量 | - | 190 GPa |
屈服强度、拉伸强度和杨氏模量的值是针对轧制方向给出的。 横向轧制的相应值大约高2%。
Jpeak J峰值 (T) | Typical specific total loss 典型特定总铁损值 (W/kg) |
50 Hz | 100 Hz | 200 Hz | 400 Hz | 700 Hz | 1000 Hz | 2500 Hz | 5000 Hz | 10000 Hz |
0.1 | 0.02 | 0.04 | 0.08 | 0.17 | 0.34 | 0.55 | 1.68 | 4.63 | 14.2 |
0.2 | 0.08 | 0.16 | 0.31 | 0.67 | 1.31 | 2.09 | 6.78 | 18.3 | 52.8 |
0.3 | 0.16 | 0.32 | 0.65 | 1.42 | 2.77 | 4.31 | 14.7 | 39.5 | 112 |
0.4 | 0.25 | 0.51 | 1.07 | 2.33 | 4.58 | 7.16 | 24.7 | 66.9 | 189 |
0.5 | 0.35 | 0.71 | 1.55 | 3.39 | 6.74 | 10.5 | 36.5 | 99.5 | 281 |
0.6 | 0.47 | 0.97 | 2.09 | 4.57 | 9.23 | 14.4 | 50.1 | 137 | 384 |
0.7 | 0.60 | 1.23 | 2.69 | 5.91 | 11.9 | 18.7 | 65.2 | 181 |
|
0.8 | 0.74 | 1.55 | 3.36 | 7.42 | 14.7 | 23.5 | 81.4 | 228 |
|
0.9 | 0.91 | 1.89 | 4.12 | 9.12 | 18.0 | 28.8 | 102 | 281 |
|
1.0 | 1.10 | 2.29 | 4.94 | 11.0 | 21.6 | 34.4 | 123 |
|
|
1.1 | 1.33 | 2.75 | 5.99 | 13.3 | 26.2 | 41.4 | 147 |
|
|
1.2 | 1.60 | 3.29 | 7.18 | 16.0 | 31.3 | 49.1 | 174 |
|
|
1.3 | 1.94 | 4.01 | 8.68 | 19.4 | 37.5 | 59.0 | 208 |
|
|
1.4 | 2.36 | 4.91 | 10.6 | 23.6 | 45.3 | 71.7 | 250 |
|
|
1.5 | 2.84 | 5.76 | 12.6 | 28.5 | 54.6 | 86.0 | 300 |
|
|
1.6 | 3.24 | 6.67 | 14.5 | 32.6 | 62.8 | 99.3 | 353 |
|
|
1.7 | 3.73 | 7.57 |
|
|
|
|
|
|
|
1.8 | 4.19 | 8.45 |
|
|
|
|
|
|
|
1.9 | 4.68 | 9.65 |
|
|
|
|
|
|
|
典型磁极化峰值(磁极化曲线)
Hpeak H峰值 (A/m) | Typical peak magnetic polarisation, Jpeak 典型磁极化峰值, J峰值(T) |
50 Hz | 100 Hz | 200 Hz | 400 Hz | 700 Hz | 1000 Hz | 2500 Hz | 5000 Hz | 10000 Hz |
20 | 0.020 | 0.019 | 0.019 | 0.019 | 0.018 | 0.018 | 0.018 | 0.017 | 0.016 |
30 | 0.04 | 0.04 | 0.04 | 0.04 | 0.03 | 0.03 | 0.03 | 0.03 | 0.02 |
50 | 0.20 | 0.20 | 0.18 | 0.17 | 0.16 | 0.16 | 0.15 | 0.11 | 0.09 |
70 | 0.55 | 0.54 | 0.52 | 0.50 | 0.47 | 0.45 | 0.29 | 0.21 | 0.17 |
100 | 0.86 | 0.86 | 0.84 | 0.84 | 0.82 | 0.80 | 0.61 | 0.37 | 0.25 |
150 | 1.10 | 1.10 | 1.09 | 1.09 | 1.09 | 1.08 | 0.99 | 0.74 | 0.48 |
200 | 1.20 | 1.20 | 1.20 | 1.20 | 1.20 | 1.19 | 1.15 | 1.02 | 0.69 |
400 | 1.35 | 1.35 | 1.35 | 1.34 | 1.34 | 1.34 | 1.34 | 1.31 | 1.18 |
800 | 1.43 | 1.43 | 1.43 | 1.43 | 1.43 | 1.43 | 1.43 | 1.42 |
|
1500 | 1.50 | 1.50 | 1.50 | 1.50 | 1.50 | 1.50 | 1.50 |
|
|
2500 | 1.56 | 1.56 | 1.56 | 1.56 | 1.56 | 1.56 | 1.56 |
|
|
5000 | 1.66 | 1.66 | 1.66 | 1.66 | 1.66 |
|
|
|
|
7500 | 1.73 | 1.73 |
|
|
|
|
|
|
|
10000 | 1.79 | 1.79 |
|
|
|
|
|
|
|
20000 | 1.91 | 1.91 |
|
|
|
|
|
|
|