0.35毫米1750H

NO35-1750H Data sheet数据表

极薄无取向电工钢

Cogent Hi-Lite NO35-1750H牌号符合EN 10303:2015和IEC 60404-8-8:2017标准中的所有要求。 在许多情况下,最小/最大性能优于上述标准中相同牌号标称厚度的等级。


Magnetic properties磁性


最小值/最大值

典型值

Specific total loss特定总铁损值 at 1.0 T and 50 Hz

-

0.88 W/kg

Specific total loss特定总铁损值 at 1.5 T and 50 Hz

-

2.11 W/kg

Specific total loss特定总铁损值 at 1.0 T and 400 Hz

Max 17.5 W/kg

16.4 W/kg

Specific total loss特定总铁损值 at 1.5 T and 400 Hz

Max 41.7 W/kg

38.8 W/kg

Specific total loss特定总铁损值 at 1.0 T and 700 Hz

Max 42.2 W/kg

39.4 W/kg

Specific total loss特定总铁损值 at 1.0 T and 2500 Hz

-

333 W/kg

Peak magnetic polarisation磁极化峰值 at 2500 A/m and 50 Hz

Min 1.52 T

1.56 T

Peak magnetic polarisation磁极化峰值 at 5000 A/m and 50 Hz

Min 1.62 T

1.65 T

Peak magnetic polarisation磁极化峰值 at 10000 A/m and 50 Hz

Min 1.74 T

1.77 T

Relative peak permeability相对峰值渗透率 at 1.5 T and 50 Hz

-

820

Relative peak permeability相对峰值渗透率 at 1.0 T and 400 Hz

-

6370

保证铁损值是最大特定总损耗,磁极化的保证值是最小磁极化峰值


物理和机械性能

标称厚度0.35 mm

密度(假设)7.60 kg / dm3


最小值/最大值

典型值

Electrical resistivity at 23 °C在23 °C的电阻率

-

59 µΩ·cm

Thermal conductivity at 23 °C在23 °C的导热系数

-

21 W/(m·K)

Thermal expansion热膨胀 0-100 °C

-

12·10-6 /°C




Yield strength屈服强度 Rp0.2

Min 400 MPa

445 MPa

Tensile strength抗拉强度 Rm

Min 500 MPa

535 MPa

Elongation at fracture断裂伸长率 A80

Min 12 %

17 %

Young’s modulus杨氏模量

-

185 GPa

屈服强度、拉伸强度和杨氏模量的值是针对轧制方向给出的。 横向轧制的相应值大约高2%。


典型特定总铁损值

J峰值

(T)

典型特定总铁损值 (W/kg)

50 Hz

100 Hz

200 Hz

400 Hz

700 Hz

1000 Hz

2500 Hz

5000 Hz

10000 Hz

0.1

0.02

0.04

0.09

0.24

0.56

1.00

4.35

13.4

39.6

0.2

0.06

0.14

0.35

0.92

2.12

3.63

15.1

45.2

133

0.3

0.13

0.29

0.73

1.93

4.39

7.49

30.9

92.0

275

0.4

0.20

0.48

1.21

3.20

7.33

12.5

51.8

156


0.5

0.29

0.69

1.76

4.73

10.9

18.7

78.1

239


0.6

0.38

0.93

2.40

6.50

15.1

26.0

111

349


0.7

0.49

1.20

3.12

8.54

19.9

34.6

151



0.8

0.61

1.49

3.93

10.8

25.6

44.6

201



0.9

0.74

1.81

4.81

13.4

32.0

56.4

261



1.0

0.88

2.17

5.76

16.4

39.4

70.0

333



1.1

1.04

2.58

6.85

19.6

47.8

85.8

424



1.2

1.23

3.04

8.08

23.2

57.4

104




1.3

1.47

3.61

9.56

27.5

68.5

125




1.4

1.77

4.34

11.4

32.8

81.4

150




1.5

2.11

5.15

13.5

38.8

96.6

177




1.6

2.41

5.85

15.5

44.5

111

204




1.7

2.68

6.53








1.8

3.02

7.18








1.9

3.46

8.07








 

典型磁极化峰值(磁极化曲线)

H峰值

(A/m)

典型磁极化峰值, J峰值 (T)

50 Hz

100 Hz

200 Hz

400 Hz

700 Hz

1000 Hz

2500 Hz

5000 Hz

10000 Hz

20

0.077

0.073

0.064

0.064

0.064

0.055

0.036

0.024

0.016

30

0.19

0.17

0.15

0.12

0.10

0.083

0.051

0.034

0.022

50

0.60

0.54

0.43

0.30

0.22

0.18

0.10

0.063

0.039

70

0.85

0.82

0.72

0.52

0.37

0.30

0.15

0.093

0.057

100

1.06

1.05

1.00

0.81

0.60

0.48

0.26

0.15

0.090

150

1.21

1.20

1.19

1.16

0.93

0.77

0.44

0.27

0.16

200

1.27

1.27

1.26

1.26

1.19

0.99

0.59

0.38

0.24

400

1.38

1.38

1.37

1.37

1.35

1.31

1.02

0.70

0.48

800

1.44

1.44

1.44

1.44

1.43

1.41

1.31



1500

1.50

1.50

1.50

1.50

1.50

1.50




2500

1.56

1.56

1.56

1.56

1.56

1.56




5000

1.65

1.65

1.65

1.65

1.65

1.65




7500

1.72

1.72








10000

1.77

1.77








20000

1.89

1.89